Oxide scale formation and microstructural degradation of conventional, Pt- and Pt/Ir-modified NiAl diffusion coatings during thermocyclic exposure at 1100 °C
موضوعات مرتبط
مهندسی و علوم پایه مهندسی مواد سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
Oxide scale formation and microstructural degradation of conventional, Pt- and Pt/Ir-modified NiAl diffusion coatings during thermocyclic exposure at 1100 °C
چکیده انگلیسی
The microstructural degradation of Pt- and Pt/Ir-modified NiAl coatings during thermocyclic exposure at 1100 °C was investigated. Detailed microstructural investigation revealed the different beneficial effects of Pt and Ir. Platinum was found to be active in the healing mechanism of the oxide scale, whereas Ir incorporation provided an obstruction to interdiffusion. Oxidized surface morphologies exhibited the formation of a dense alumina scale on top of the PtAl coating, whereas Al-depletion in the NiAl coating was accelerated due to scale spallation and interfacial void formation. Additionally, Pt inward- and Ni outward diffusion was substantially reduced in the Ir-containing coatings.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Corrosion Science - Volume 144, November 2018, Pages 313-327
نویسندگان
, , ,