- We present UCS and filtration stability of cement grouts at different temperatures.
- It includes UCS of 96, filtration stability of 36 and permeability of 4 specimens.
- UCS of grout specimens prepared and cured at 8Â Â°C is lower than those at 20Â Â°C.
- Filtration stability of cement grouts at 8Â Â°C is almost the same as that at 20Â Â°C.
The overall objective of this work, carried out under the research project “True Improvement in Grouting High pressure Technology for tunnelling (TIGHT)” is to understand the behavior of cement grouts under true tunnelling conditions. This paper describes a systematic laboratory study to characterize uniaxial compressive strength (UCS) and filtration stability of grouts made up of three types of cement commonly used for tunnel grouting in the Nordic countries. Since in-situ tunnel conditions are different from those of the laboratory in terms of temperature, we made various cement grouts at different temperatures and tested in the laboratory. The water cement ratios of 0.6, 0.8, 1.0 and 1.2 were used for all three cements and grouts were made and cured at two temperatures; 8Â Â°C and 20Â Â°C. Strength of a total of 96 cylindrical specimens of 4 and 7Â days age and permeability of four specimens of 7Â days age were measured. Filtration tests were done for 36 cement grouts. Results of the laboratory tests show that strength of samples cured at 8Â Â°C is lower than those cured at 20Â Â°C. Strength of grout specimens decreases dramatically with increasing w/c ratio. Filtration of cement grouts at 8Â Â°C is not that different from those at 20Â Â°C and filtration stability increases with increasing water-cement ratio. Permeability of cylindrical specimens of different types of cement varies several orders of magnitude; from nano- to milli-Darcy.
Journal: Tunnelling and Underground Space Technology - Volume 71, January 2018, Pages 193-200