- Injectable dextran hydrogels are prepared by metal-free click chemistry.
- Azadibenzocyclooctyne-azide click chemistry is practical to prepare the hydrogel.
- Click-crosslinked dextran hydrogels possess low cytotoxicity in chondrocytes.
- Chondrocyte spheroids yield a high content of cartilage matrices in the hydrogel.
- Injectable dextran hydrogels have high potential for cartilage tissue engineering.
Injectable dextran-based hydrogels were prepared for the first time by bioorthogonal click chemistry for cartilage tissue engineering. Click-crosslinked injectable hydrogels based on cyto-compatible dextran (Mw = 10 kDa) were successfully fabricated under physiological conditions by metal-free alkyne-azide cycloaddition (click) reaction between azadibenzocyclooctyne-modified dextran (Dex-ADIBO) and azide-modified dextran (Dex-N3). Gelation time of these dextran hydrogels could be regulated in the range of approximately 1.1 to 10.2 min, depending on the polymer concentrations (5% or 10%) and ADIBO substitution degree (DS, 5 or 10) of Dex-ADIBO. Rheological analysis indicated that the dextran hydrogels were elastic and had storage moduli from 2.1 to 6.0 kPa with increasing DS of ADIBO from 5 to 10. The in vitro tests revealed that the dextran hydrogel crosslinked from Dex-ADIBO DS 10 and Dex-N3 DS 10 at a polymer concentration of 10% could support high viability of individual rabbit chondrocytes and the chondrocyte spheroids encapsulated in the hydrogel over 21 days. Individual chondrocytes and chondrocyte spheroids in the hydrogel could produce cartilage matrices such as collagen and glycosaminoglycans. However, the chondrocyte spheroids produced a higher content of matrices than individual chondrocytes. This study indicates that metal-free click chemistry is effective to produce injectable dextran hydrogels for cartilage tissue engineering.
107
Journal: Materials Science and Engineering: C - Volume 73, 1 April 2017, Pages 21-30