Microwave-assisted sintering of Al2O3-MWCNT nanocomposites
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Alumina-MWCNT composite was densified by microwave sintering. CNTs were coated with boehmite nanoparticles to enhance their distribution in composite samples. Calcination temperature of composite powder was determined by TGA analysis (5 °C/min). Samples containing 0 and 1vol%CNT were produced by cold isostatic pressing at 180 MPa. Microwave sintering (1520 °C for 45 min) was conducted under the flow of argon. Phase analysis of the calcined composite powder showed complete transformation of boehmite into gamma-alumina. The relative densities were 99.3% and 98.1% for monolithic alumina and composite, respectively. CNT addition improved the fracture toughness of alumina by ~37%. SEM images showed that microwave sintering was successful. Also, coating CNTs improved their distribution in the alumina matrix.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 43, Issue 8, 1 June 2017, Pages 6105-6109
Journal: Ceramics International - Volume 43, Issue 8, 1 June 2017, Pages 6105-6109
نویسندگان
Hossein Ghobadi, Touradj Ebadzadeh, Zahra Sadeghian, Hadi Barzegar-Bafrooei, Ali Nemati,