Enhanced energy storage performance of Ba0.4Sr0.6TiO3 ceramics: Influence of sintering atmosphere
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
سرامیک و کامپوزیت
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Ba0.4Sr0.6TiO3 (BST) powders were prepared by hydrothermal method, the ceramics were sintered in N2, air and O2 atmosphere respectively. The effect of sintering atmosphere on the microstructure, dielectric properties, and energy storage performance of BST ceramics were investigated. The grain size of the BST ceramics sintered in O2 atmosphere was reduced to 0.44 µm, indicating the grain growth was significantly inhibited with increasing oxygen partial pressure due to the lack of oxygen vacancy. Dielectric relaxation behavior was observed in the BST ceramics, and the degree of which was increased with increasing oxygen partial pressure. BST ceramics sintered in O2 atmosphere showed the largest critical breakdown strength of 16.72 kV/mm, at which the highest energy storage density of 1.081 J/cm3 and a moderate energy storage efficiency of (73.78%) were obtained. The dependence of energy-storage properties on applied field was also investigated, it was found that the energy storage density increased with increasing applied filed while the energy storage efficiency decreased with increasing applied filed.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Ceramics International - Volume 43, Supplement 1, August 2017, Pages S232-S238
Journal: Ceramics International - Volume 43, Supplement 1, August 2017, Pages S232-S238
نویسندگان
Qian Jin, Yong-Ping Pu, Chun Wang, Zi-Yan Gao, Han-Yu Zheng,