- The physical properties of molten (ZrO2)x(Al2O3)1-x (x = 0.356 and 0.172) have been evaluated.
- The measurement was conducted using an aerodynamic levitation technique.
- The density and viscosity were measured.
During a molten core-concrete interaction, molten oxides consisting of molten core materials (UO2 and ZrO2) and concrete (Al2O3, SiO2, CaO) are formed. Reliable data on the physical properties of the molten oxides will allow us to accurately predict the progression of a nuclear reactor core meltdown accident. In this study, the viscosities and densities of molten (ZrO2)x(Al2O3)1-x (x = 0.356 and 0.172) were measured using an aerodynamic levitation technique. The densities of two small samples were estimated from their masses and their volumes (calculated from recorded images of the molten samples). The droplets were forced to oscillate using speakers, and their viscosities were evaluated from the damping behaviors of their oscillations. The results showed that the viscosity of molten (ZrO2)x(Al2O3)1-x compared to that of pure molten Al2O3 is 25% lower for x = 0.172, while it is unexpectedly 20% higher for x = 0.356.
Journal: Journal of Nuclear Materials - Volume 487, 15 April 2017, Pages 121-127