Effects of oil on gelcasting of oil-in-water Si3N4 suspensions
دانلود مقاله + سفارش ترجمه
دانلود مقاله ISI انگلیسی
رایگان برای ایرانیان
کلمات کلیدی
موضوعات مرتبط
مهندسی و علوم پایه
مهندسی مواد
فلزات و آلیاژها
پیش نمایش صفحه اول مقاله
چکیده انگلیسی
Porous Si3N4 ceramics were fabricated through gelcasting followed by pressureless sinter at 1690 °C. Oil-in-water (O/W) Si3N4 suspensions were prepared by mixing paraffin O/W emulsion and Si3N4 suspensions, sodium alginate was used as gelling agent. The casted suspensions were quickly gelled by spraying calcium chloride aqueous solution onto the surface, thus oil was enwrapped into the green bodies. The porous Si3N4 ceramics had spherical-shaped pores both with and without adding O/W emulsion. As changing the O/W emulsion content in the suspension, porous Si3N4 ceramics with high open porosity of 60.1-63.9% and flexural strength of 44.5-34.6 MPa were obtained.
ناشر
Database: Elsevier - ScienceDirect (ساینس دایرکت)
Journal: Journal of Alloys and Compounds - Volume 699, 30 March 2017, Pages 268-273
Journal: Journal of Alloys and Compounds - Volume 699, 30 March 2017, Pages 268-273
نویسندگان
Feng Wang, Jinwei Yin, Dongxu Yao, Yongfeng Xia, Kaihui Zuo, Hanqin Liang, YuPing Zeng,