Optimizing the structure and properties of Y2O3 stabilized zirconia: An atmospheric plasma spray (APS) and solution precursor plasma spray (SPPS) based comparative study

The yttria stabilized zirconia (8%YSZ) is widely used to insulate the metallic components of the engine from high temperature and improve the operating temperature of gas turbine engines. With different processing parameters, 8YSZ coatings are prepared by atmospheric plasma spray (APS) and solution precursor plasma spray (SPPS) techniques and the microstructural features and thermodynamics properties are compared. The electron back scattered diffraction (EBSD) analysis indicate that the substitutional point defects (Zr0.86Y0.14O1.93) in the 8YSZ APS coatings are considerably higher than the corresponding SPPS coatings. The replacement of Zr4+ by Y3+ disturbs the charge neutrality of the system which might be compensated by the creation of oxygen vacancy. Both the substitutional point defects and the oxygen vacancies are the sources of phonon scattering, modifying the thermal conductivity of the coating. Pores and cracks are qualitatively and quantitatively analyzed in the microstructure of 8YSZ coatings. Strain tolerant and high thermal cycling life coatings are prepared by SPPS due to the existence of vertical cracks in the microstructure. Comparing the thermal insulation properties of the coatings, the APS coating provided lower thermal conductivities relative to the SPPS coatings which might be due to the high concentration of point defects and low concentration of the mixed oxide phase.