10227046 | Corrosion Science | 2018 | 27 Pages |
Abstract
In this study, the degradation behavior of Al2O3-Ti3AlC2-Si-C refractories and a complete degradation process of Ti3AlC2 under a temperature gradient along the penetration direction were investigated by a dynamic corrosion at approximately 1630â°C. The degradation process of Ti3AlC2 affected the local liquid components by assisting to form CaAl12O19 and restrained CaO penetration via trapping into high-melting phase. On refractories-steel/slag interfaces affected by Marangoni convection, the molten steel penetration was suppressed in the samples with Ti3AlC2. A refined texture and increased viscosity, accompanying Ti3AlC2 oxidation and dissolution in molten steel, blocked the pathways and restrained the penetration of molten steel.