Abstract
The corrosion behavior of mild steel and mild steel covered by electrochemically deposited (a) polyaniline (PANI) film, (b) epoxy coating and (c) PANI/epoxy coating system in 0.1Â M sulfuric acid solution were investigated by electrochemical impedance spectroscopy (EIS). Electrochemical deposition of PANI film was performed from aqueous solution of 0.5Â M sodium benzoate and 0.1Â M aniline at constant current density of 1.5Â mAÂ cmâ2. Epoxy coatings on mild steel and mild steel modified by PANI film were deposited at constant voltage. It was shown that thin PANI film had provided good corrosion protection of mild steel in 0.1Â M sulfuric acid solution, and could be used for modification of mild steel prior to epoxy coating deposition. The increased corrosion protection of mild steel by PANI/epoxy coating system in the same solution was obtained.
Related Topics
Physical Sciences and Engineering
Chemical Engineering
Process Chemistry and Technology
Authors
M.M. PopoviÄ, B.N. Grgur, V.B. MiÅ¡koviÄ-StankoviÄ,