| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 10634220 | Scripta Materialia | 2005 | 5 Pages |
Abstract
Cu-based bulk metallic glass matrix composites (BMGMCs) containing in-situ TiC particles were fabricated successfully. The yield and fracture strength increased from 1930Â MPa, 2250Â MPa to 2210Â MPa, 2500Â MPa, respectively. The ductility was improved and the hardness was also enhanced by 25%. The fracture mechanism was investigated in detail.
Related Topics
Physical Sciences and Engineering
Materials Science
Ceramics and Composites
Authors
Huameng Fu, Haifeng Zhang, Hao Wang, Qingsheng Zhang, Zhuangqi Hu,