Abstract
La conversion coatings in various growth stages were obtained by immersing hot-dip galvanized (HDG) sheets in the lanthanum nitrate solution for different times from 10Â s to 240Â min. A growth process model of the La conversion coating on hot-dip galvanized steel was suggested. It is shown that the conversion coating grows more quickly by the zinc grain boundaries, where the cracks occur first and develop gradually on the whole surface of the conversion coating. When the immersion time is increased (more than 60Â min), some rod-like precipitations containing more Zn and less La are deposited on the conversion coating. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) measurement results reveal that, with increasing immersion time, the protective property of the La conversion coatings is gradually increased in the early growth stage and then decreased when the cracks develop.
Related Topics
Physical Sciences and Engineering
Materials Science
Nanotechnology
Authors
Shuang-hong Zhang, Gang Kong, Jin-tang Lu, Chun-shan Che, Ling-yan Liu,