Preparation of hierarchical layer-stacking Mn-Ce composite oxide for catalytic total oxidation of VOCs

Hierarchical layer-stacking Mn-Ce composite oxide with mesoporous structure was firstly prepared by a simple precipitation/decomposition procedure with oxalate precursor and the complete catalytic oxidation of VOCs (benzene, toluene and ethyl acetate) were examined. The Mn-Ce oxalate precursor was obtained from metal salt and oxalic acid without any additives. The resulting materials were characterized by X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), hydrogen temperature programmed reduction (H2-TPR) and X-ray photoelectron spectroscopy (XPS). Compared with Mn-Ce composite oxide synthesized through a traditional method (Na2CO3 route), the hierarchical layer-stacking Mn-Ce composite oxide exhibited higher catalytic activity in the complete oxidation of volatile organic compounds (VOCs). By means of testing, the data revealed that the hierarchical layer-stacking Mn-Ce composite oxide possessed superior physiochemical properties such as good low-temperature reducibility, high manganese oxidation state and rich adsorbed surface oxygen species which resulted in the enhancement of catalytic abilities.

The activities for VOCs oxidation over the hierarchical layer-stacking Mn-Ce oxide with porous structure were promotedFigure optionsDownload full-size imageDownload as PowerPoint slide