Hydrothermal synthesis, crystal structure and physical properties of a new gadolinium phosphite hydrate

A new compound Gd4(H2O)5(HPO3)6 (1) was isolated from the reaction of gadolinium chloride GdCl3 · nH2O with H3PO3 under hydrothermal conditions. The crystal structure was solved by means of single-crystal X-ray diffraction. The structure is composed of parallel gadolinium–oxygen polyhedra chains connected by phosphite ions, and shows three-dimensional (3D) open-framework with eight-membered ring (8MR) channels. The structure is different from its counterpart Eu2(H2O)2.5(PO3H)3 due to the effect of lanthanide contraction. The intensive intrinsic UV emission of this compound at λmax = 312 nm comes from the spin-forbidden 6P7/2 → 8S7/2 f–f transition of the Gd3+ ions. No magnetic order was observed for this compound.

A new compound Gd4(H2O)5(HPO3)6 was obtained by hydrothermal methods. The crystal structure is built up of parallel gadolinium–oxygen polyhedra chains connected into three-dimensional (3D) open-framework by phosphite ions, showing eight-membered ring channels. The compound shows intrinsic intensive UV emission around 312 nm and no magnetic order was observed.Figure optionsDownload full-size imageDownload as PowerPoint slide