The influence on the mechanical response by incorporation of oligostyrene-modified montmorillonite (MMT) and oligostyrene-modified bentonite (BET) into star shaped styrene–butadiene block copolymer has been investigated. The modified silicates are highly intercalated with a gallery distance of more than 9 nm and partly exfoliated. The array of tactoids consisting of 1–8 layers showing uniform state of distribution as revealed from TEM. The layers of the modified MMT and BET are observed to undergo nano-confinement, i.e. restricted to the PS-domains of the styrene–butadiene star block copolymer with impinging/bridging effects of silicate layers through the SB soft phase. DMA studies have showed an appreciable shift of the glass transition temperatures of PB- and PS-rich phases towards higher temperatures in addition to an increase of the storage modulus due to nanoclay reinforcement. Generally the Young’s modulus and yield stress was strongly increased with the incorporation of modified nanoparticles whereas at the same time the strain at break reduces slightly. The elastic–plastic hysteresis–stress and the hysteresis–work are largely increased due to effective interfacial effect; an effect that is largely attributed to the presence of highly intercalated and partially exfoliated silicate layers. The extent of increase was more in the modified MMT than in the modified BET based nanocomposites. The stress-decay and the strain-recovery aspects have also been critically analyzed in relation to their micro-structural attributes. Our study fundamentally demonstrates two critical aspects related to mechanical properties and particularly with regard to elastic–plastic hysteresis response. Firstly, partial confinement of the silicate layers is promoted by PS-aided surface modification facilitating enhancement in mechanical properties and secondly, the nano-confinement of modified MMT seems to be more effective in improving the hysteresis performance when compared to BET with higher charge density.
Graphical abstractThe figure illustrates the substantial enhancement in mechanical hysteresis (elastic–plastic regime) as indicated by the increase in the hysteresis-work due to incorporation of oligostyrene modified layered silicates into S/B based star block copolymer matrix (ST3) via self-assembly induced nano-confinement effects.Figure optionsDownload full-size imageDownload as PowerPoint slide