Effect of monomer molecular flow on electrode surface on the structure of poly(α-tetrathiophene) obtained by anodic polymerization

Different structures have been found for poly(α-tetrathiophene) [poly(α-4TF)] electrosynthesized on Pt by anodic oxidation of 1.0 mM monomer solutions in media such as 45:35:20 (v/v/v) acetonitrile/THF/DMF, 45:35:20 (v/v/v) acetonitrile/ethanol/DMF and 72:28 (v/v) acetonitrile/DMF containing 0.1 M LiClO4; as well as 72:28 (v/v) acetonitrile/DMF with 0.1 M NaClO3, under dynamic and static conditions at 25 °C. In all cases the polymer was generated by chronoamperometry at 1.000 V vs. Ag∣AgCl, corresponding to the first oxidation peak detected by cyclic voltammetry. Uniform, adherent, insoluble and black polymer films were obtained under these conditions. The resulting structures have been elucidated by combining the information of their IR spectrum, nox-value and doping level of the counterion. The degree of crosslinking of every polymer has been quantified and related to the molecular flow of monomer on the Pt electrode. A monomer concentration flow between 4 × 10−6 and 5 × 10−6 mmol cm−2 s−1 was determined as the limiting value below which the polymer grows with crosslinking. This value corresponds to the electropolymerization rate of α-4TF by Pt area unit at 25 °C.