Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
1429077 | Materials Science and Engineering: C | 2013 | 13 Pages |
Commercially pure titanium plates/coupons and pure titanium powders were soaked for 24 h in 5 M NaOH and 5 M KOH solutions, under identical conditions, over the temperature range of 37° to 90 °C. Wettability of the surfaces of alkali-treated cpTi coupons was studied by using contact angle goniometry. cpTi coupons soaked in 5 M NaOH or 5 M KOH solutions were found to have hydrophilic surfaces. Hydrous alkali titanate nanofibers and nanotubes were identified with SEM/EDXS and grazing incidence XRD. Surface areas of Ti powders increased > 50–220 times, depending on the treatment, when soaked in the above solutions. A solution was developed to coat amorphous calcium phosphate, instead of hydroxyapatite, on Ti coupon surfaces. In vitro cell culture tests were performed with osteoblast-like cells on the alkali-treated samples.
Graphical abstractFigure optionsDownload full-size imageDownload as PowerPoint slideHighlights► Titanium was treated with 5 M NaOH and 5 M KOH alkali solutions at 37°, 60° and 90 °C. ► Treated Ti was compared with contact angle, GI-XRD, BET, SEM and cell culture tests. ► A calcification solution was developed for coating Ti at 37°C with amorphous CaP.