Gallium-containing phosphosilicate glasses: Functionalization and in-vitro bioactivity

•Silanization of Ga-containing phosphosilicate glasses was performed.•Glass surface enrichment with OH and NH2 groups was obtained.•Optimization of functionalization was realized.•In vitro bioactivity investigation of glasses and before and after functionalization.•TEOS functionalization better as compared to APTS one for bioactivity response.

A gallium containing glass 45.7SiO2·24.1Na2O·26.6CaO·2.6P2O5·1.0Ga2O3 (referred to as “Ga1.0”) and a parent Ga-free glass 46.2SiO2·24.3Na2O·26.9CaO·2.6P2O5 (hereinafter represented as “H”), corresponding to Bioglass® 45S5, were functionalized with Tetraethoxysilane (TEOS) and (3-Aminopropyl)triethoxysilane (APTS) in order to improve their ability to bond with biomolecules, such as drugs, proteins, and peptides. Functionalization with TEOS and APTS promoted the increment in OH groups and formation of NH2 groups on the glass surface, respectively. The presence of OH or NH2 groups was investigated by means of IR spectroscopy and elemental analysis. Moreover, in vitro study of these functionalized glasses was performed in simulated body fluid (SBF) so as to investigate the effect of functionalization on the bioactive behavior of H and Ga1.0. The results showed that the functionalization was obtained along with maintaining their bioactivity. The surfaces of both functionalized glasses were covered by a layer of apatite within 30 days of SBF immersion. In addition, CaCO3 was also identified on the surface of APTS functionalized glasses. However, no gallium release was detected during SBF soaking.