Localized corrosion and effects of pre-passivation treatment of Nitinol and SS304 orthodontic wires in simulated saliva solution in the presence and absence of fluoride ions were investigated by means of potentiodynamic and potentiostatic polarisations. Results revealed that Nitinol does not show pitting corrosion in saliva solution however, SS304 shows pitting corrosion. Meanwhile fluoride ion has deteriorative effect on pitting corrosion of Nitinol, while its effect on SS304 was marginally constructive. Additionally, the presence of artificial crevice has no effect on corrosion behaviour in the presence of fluoride. Pre-passivation treatment has positive influence on pitting corrosion of both alloys in the presence of F− ions.
► Localized corrosion of NiTi and SS304 orthodontic wires was investigated. ► Effect of fluoride ions on the pitting corrosion was deteriorative. ► Fluoride ions have no considerable effect on crevice corrosion. ► Pre-passivation has positive effect on pitting corrosion in the presence of fluoride.