Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
1430717 | Materials Science and Engineering: C | 2009 | 9 Pages |
Porous hydroxyapatite (HA) scaffold has great potential in bone tissue engineering applications. A new method to fabricate macroporous calcium phosphate (CP) scaffold via microwave irradiation, followed by conventional sintering to form HA scaffold was developed. Incorporation of trisodium citrate dihydrate and citric acid in the CP mixture gave macroporous scaffolds upon microwave rapid drying. In this work, a mixture of β-tricalcium phosphate (β-TCP), calcium carbonate (CaCO3), trisodium citrate dihydrate, citric acid and double distilled de-ionised water (DDI) was exposed to microwave radiation to form a macroporous structure. Based on gross eye examinations, addition of trisodium citrate at 30 and 40 wt.% in the CP mixture (β-TCP and CaCO3) without citric acid indicates increasing order of pore volume where the highest porosity yield was observed at 40 wt.% of trisodium citrate addition and the pore size was detected at several millimeters. Therefore, optimization of pore size was performed by adding 3–7 wt.% of citric acid in the CP mixture which was separately mixed with 30 and 40 wt.% of trisodium citrate for comparison purposes. Fabricated scaffolds were calcined at 600 °C and washed with DDI water to remove the sodium hydroxycarbonate and sintered at 1250 °C to form HA phase as confirmed in the X-ray diffraction (XRD) results. Based on Archimedes method, HA scaffolds prepared from 40 wt.% of trisodium citrate with 3–7 wt.% of citric acid added CP mixture have an open and interconnected porous structure ranging from 51 to 53 vol.% and observation using Scanning electron microscope (SEM) showed the pore size distribution between 100 and 500 μm. The cytotoxicity tests revealed that the porous HA scaffolds have no cytotoxic potential on MG63 osteoblast-like cells which might allow for their use as biomaterials.