Structure and thermal conductivity of powder injection molded AlN ceramic

AlN powders doped with Y2O3 (5 wt.%) were compacted by employing powder injection molding (PIM) technique. The binder consisted of paraffin wax (PW, 60 wt.%), polypropylene (PP, 35 wt.%) and stearic acid (SA, 5 wt.%). The feedstock was prepared with a solid loading of 62 vol.%. The binder was removed through debinding process in two steps, solvent debinding followed by thermal debinding. At last, the debound samples were sintered in flowing nitrogen gas at atmospheric pressure. The result reveals that thermal debinding atmosphere has significant effect on the thermal conductivity and structure of AlN ceramics. The thermal conductivity of injection molded AlN ceramics thermal debound in flowing nitrogen gas is 231 W m−1 K−1.