Atomistic simulations are used to investigate how the nanoindentation mechanism influences dislocation nucleation under molecular dynamic behavior on the aluminum (0 0 1) surface. The characteristics of molecular dynamics in terms of various nucleation criteria are explored, including various molecular models, a multi-step load/unload cycle, deformation mechanism of atoms, tilt angle of the indenter, and slip vectors. Simulation results show that both the plastic energy and the adhesive force increase with increasing nanoindentation depths. The maximum forces for all indentation depths decrease with increasing multi-step load/unload cycle time. Dislocation nucleation, gliding, and interaction occur along Shockley partials on (1 1 1) slip planes. The indentation force applied along the normal direction, a tilt angle of 0°, is smaller than the force component that acts on the surface atoms. The corresponding slip vector of the atoms in the (1 1 1) plane has low-energy sessile stair-rod dislocations in the pyramid of intrinsic stacking faults.