Properties of self-compacting concrete prepared with recycled glass aggregate

The effects of recycled glass (RG) cullet on fresh and hardened properties of self-compacting concrete (SCC) were investigated. RG was used to replace river sand (in proportions of 10%, 20% and 30%), and 10 mm granite (5%, 10% and 15%) in making the SCC concrete mixes. Fly ash was used in the concrete mixes to suppress the potential alkali-silica reaction. The experimental results showed that the slump flow, blocking ratio, air content of the RG–SCC mixes increased with increasing recycled glass content. The compressive strength, tensile splitting strength and static modulus of elasticity of the RG–SCC mixes were decreased with an increase in recycled glass aggregate content. Moreover, the resistance to chloride ion penetration increased and the drying shrinkage of the RG–SCC mixes decreased when the recycled glass content increased. The results showed that it is feasible to produce SCC with recycled glass cullet.