| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 1458563 | Ceramics International | 2016 | 8 Pages |
Commercial stone wool fibres were modified with copper(II) oxide coatings. This oxide is widely used in processes of surface modification for filter materials to improve its bacterial retention. The microorganisms are already susceptible to low concentrations of copper in contrast to humans for which copper is an inert material in the concentration range. Additionally, the coatings changed the electrokinetic properties of the fibres. As a result, the isoelectric point (IEP) of the untreated fibres was shifted from acidic towards a more basic pH range. A positive or no charge on the surface of the fibres allows them to be a substrate for the positively charged adsorbents of negatively charged waterborne contaminants with the use of electrostatic adsorption. The coatings were prepared by dip coating with the use of two different coating precursors: the aqueous suspension of CuO nanoparticles and aqueous solutions of copper(II) nitrate trihydrate or copper(II) acetate or a mixture of thereof. The zeta potential of the modified fibres was determined by a streaming potential method. The adhesion of the coatings was tested by flushing and ultrasonication of the modified fibres. The isoelectric point of the fibres was shifted towards a more basic pH range for all precursors with the largest impact of the copper(II) nitrate trihydrate precursor. This coating changed the IEP of the fibres from 4.1 to 8.3 pH value. The highest calculated coverage of the coatings was in the range of 54% and was obtained by using copper(II) nitrate trihydrate/CuO nanoparticles precursor. Although, we do not predict such modified fibres to act as a standalone water filter, we believe they have the potential to be an excellent support material for active adsorbents.