Nanocrystalline gamma alumina (γ-Al2O3) powder with a crystallite size of ~10 nm was synthesized by oxidation of high purity aluminium plate in a humid atmosphere followed by annealing in air. Spark plasma sintering (SPS) at different sintering parameters (temperature, dwell time, heating rate, pressure) were studied for this highly porous γ-Al2O3 in correlation with the evolution in microstructure and density of the ceramics. SPS sintering cycles using different heating rates were carried out at 1050–1550 °C with dwell times of 3 min and 20 min under uniaxial pressure of 80 MPa. Alumina sintered at 1550 °C for 20 min reached 99% of the theoretical density and average grain size of 8.5 µm. Significant grain growth was observed in ceramics sintered at temperatures above 1250 °C.