Joining of Si3N4 to Si3N4 using a AuPd(Co, Ni)–V filler alloy and the interfacial reactions

Au38.0–Pd28.0–Co18.0–Ni7.0–V9.0 (in wt%) alloy was designed as a filler for joining Si3N4. The filler alloy showed a contact angle of 77.2° on Si3N4 ceramic at 1473 K. The Si3N4/Si3N4 joint brazed with the rapidly-solidified filler foils at 1443 K for 10 min exhibits an average three-point bend strength of 320.7 MPa at room temperature and the strength values are 217.9 MPa and 102.9 MPa at 1073 K and 1173 K respectively. The interfacial reaction products were composed of V2N and Pd2Si, and the elements Co and Ni in the brazing alloy did not participate in the interfacial reactions. The coarse-network-like distribution of refractory Pd2Si compound within the Au–Pd–Co–Ni alloy matrix throughout the joint contributes to the stable high-temperature joint strengths.