Microstructure and oxidation resistance of Si–Mo–B coating for C/SiC coated carbon/carbon composites

A self-sealing Si–Mo–B oxidation resistance coating was prepared on C/SiC coated carbon/carbon (C/C) composites by slurry and high temperature treatment method. The oxidation resistance of the coating increases at 1173 K and first increases then decreases at 1873 K with the increase of B content from 0 to 20 wt.%. The C/SiC/gradient Si–Mo–B multilayer coating can protect C/C composite from oxidation for 100 h at 1173 K and 125 h at 1873 K. The good oxidation resistance of the coating in broad temperature range could be attributed to its good self-sealing property.