Arc ion plating had been employed on a cobalt-base superalloy K40S to deposit a NiCrAlYSi coating to improve its oxidation resistance at 1323–1423 K in air. The K40S superalloy had poor oxidation resistance because a non-protective and easy spalling surface oxides scale mixed of Cr2O3 and CoCr2O4 was formed on its surface. After coated with NiCrAlYSi coating, a dense and protective α-Al2O3 scale was formed on the coating and excellently improved its oxidation resistance. Inter-diffusion obviously occurred between the coating and the substrate K40S superalloy in oxidation process, which resulted from Co atoms in K40S outwards diffused. A richen Cr and W carbides inter-diffusion layer was formed, which could acted as a diffusion barrier that barred Al atoms in coating inwards diffusion. Though the NiCrAlYSi changed into NiCoCrAlYSi during oxidation process, it still possessed a good oxidation resistance and had a considerable long-term life.

Related Topics
Physical Sciences and Engineering Materials Science Ceramics and Composites
Authors
, , , ,