Structural and electrical properties of 0.57PSN-0.43PT ceramics prepared by mechanochemical synthesis and sintered at low temperature

The effects of the poling field on the structural and electrical properties of the 0.57PSN-0.43PT ceramics were investigated. The results show that the ratio of the monoclinic to the tetragonal phases is influenced by the application of the poling electric field. The non-poled ceramics contain 71% of the monoclinic phase and 29% of the tetragonal phase. The highest d33, kp and kt were measured for ceramics poled at an electric field of 3 kV/mm. For these poled ceramics a phase determination of 86% monoclinic phase and 14% tetragonal phase was obtained from Rietveld refinements.