•Seven sodium-yttrium-silicate glass compositions were synthesised.•Thermal, hydrolytical and electrical properties of the glasses are reported.•The glasses possess the high conductivity (2 ∗ 10− 3 S/cm).•Hydrolytical resistance increases with growth of Y2O3 content.
The influence of yttrium oxide on the transport properties and chemical stability of sodium silicate glasses is investigated. The seven sodium-yttrium silicate glass compositions were synthesised. There are three composition with Na2O/Y2O3 = 6.5 and four with permanent Na2O content with 5 to 8 mol% of Y2O3. The thermal behaviour of the glasses was studied with dilatometric and DSC methods. The research into the electrical characteristics of the glass has shown that their electrical conductivity is in the range of 5 × 10− 8–10− 6 S/cm at 25 °C and 10− 3 S/cm at 300 °C. It is shown that the hydrolytic resistance increases when growing the Y2O3 concentration in the glass composition at constant Na2O content.