Multistep impregnation method for incorporation of high amount of titania into SBA-15

A multistep impregnation method was employed to incorporate high amount of titania into the mesoporous SBA-15 silica. No damage to the SBA-15 silica mesostructures was caused by the loading of titania in every cycle. The existence of titania small nanodomains were confirmed to be present by Raman spectra and UV–vis DRS measurements. High dispersion of them was realized via this method according to the results of low-angle X-ray powder diffraction (XRD), transmission electron microscopy (TEM) and N2 sorption measurements. Importantly, no blockage of mesostructures was acknowledged with titania content up to 24.4 wt.%. In comparison, normally used one-step impregnation method led to serious blockage of mesopores as the results of formation of bulk titania particles in the mesochannels. Photo-activity test for the removal of oestrogen showed the superiority of the materials synthesized by multistep impregnation method to one-step impregnation method.