Studies of solution deposited cerium oxide thin films on textured Ni-alloy substrates for YBCO superconductor

Cerium oxide (CeO2) buffer layers play an important role for the development of YBa2Cu3O7−x (YBCO) based superconducting tapes using the rolling assisted biaxially textured substrates (RABiTS) approach. The chemical solution deposition (CSD) approach has been used to grow epitaxial CeO2 films on textured Ni–3 at.% W alloy substrates with various starting precursors of ceria. Precursors such as cerium acetate, cerium acetylacetonate, cerium 2-ethylhexanoate, cerium nitrate, and cerium trifluoroacetate were prepared in suitable solvents. The optimum growth conditions for these cerium precursors were Ar–4% H2 gas processing atmosphere, solution concentration levels of 0.2–0.5 M, a dwell time of 15 min, and a process temperature range of 1050–1150 °C. X-ray diffraction, AFM, SEM, and optical microscopy were used to characterize the CeO2 films. Highly textured CeO2 layers were obtained on Ni–W substrates with both cerium acetate and cerium acetylacetonate as starting precursors. YBCO films with a Jc of 1.5 MA/cm2 were obtained on cerium acetylacetonate-based CeO2 films with sputtered YSZ and CeO2 cap layers.