•Er3+/Yb3+ codoped tellurite glass with Ag NPs was prepared by melt-quenching method.•Ag NPs with mean diameter of ∼11.4 nm was synthesized in glass heat-treated for 24 h at 370 °C.•The synthesized Ag NPs greatly enhanced 1.53 μm band fluorescence intensity of Er3+.•The fluorescence improvement was mainly attributed to the enhanced local field induced by Ag NPs.•The enhanced field was demonstrated by comparing the emission spectra of hypersensitive probe Eu3+.
Improving the spectroscopic properties of rare earth (RE) doped glass materials is a challenging task. In the present work the metallic silver nanoparticles (Ag NPs) were embedded into Er3+/Yb3+ codoped tellurite glasses with composition TeO2–Bi2O3–TiO2, prepared using melt-quenching and subsequent heat-treated techniques, and the improved effect of Ag NPs on the 1.53 μm band fluorescence of Er3+ ions was investigated. About 24 h heat-treatment of Er3+/Yb3+ codoped tellurite glass containing 1 mol % amount of AgNO3 at the temperature 370 °C yielded the well-dispersed and near-spherical Ag NPs with ∼11.4 nm average diameter as evidenced by transmission electron microscopy (TEM) image. The intense 1.53 μm band fluorescence was observed in the prepared Er3+/Yb3+ codoped tellurite glasses under the excitation of 980 nm and was further improved with the presence of Ag NPs in the glass matrix, which is attributed to the enhanced local electric field around doped RE ions induced by Ag NPs and the possible energy transfer from Ag NPs to Er3+ ions. The enhanced local electric field was well demonstrated by comparing the variation of emission spectra of hypersensitive probe Eu3+ ions in tellurite glasses with and without Ag NPs. From the Judd-Ofelt analysis, it was also found that the value of Ω6Ω6 intensity parameter increased slightly with the increase of Ag NPs concentration in a certain range, also confirming the possibility of realizing strong fluorescence emission. In addition, the amorphous structural nature was demonstrated by the measured X-ray diffraction (XRD) patterns with no sharp diffraction peak. The enhanced 1.53 μm band fluorescence indicates that the Er3+/Yb3+ codoped tellurite glass with an appropriate amount of Ag NPs is a promising candidate for the development of Er3+-doped fiber amplifiers (EDFAs) applied in the WDM systems.