•Large-area inverse-opal structures were prepared in a bulk chalcogenide glass.•Spin-coating is used to infill silica opal which is then transferred on bulk glass.•Inverse-opal structures stop-bands are consistent with effective refractive index.•Low-cost deposition and quality control of inverse structures in the glass is done.
Large (cm × cm), uniform-thickness areas of an inverse-opal photonic crystal and an inverse-opal monolayer were fabricated in a high-refractive-index As30S70 chalcogenide glass. We have developed an effective low-cost, solution-based process for fabrication of photonic structures in chalcogenide glass from silica-colloidal-crystal thin-film templates (multi- and monolayer). The chalcogenide-glass solution is spin-coated over the silica-opal film template and the infilled composite structure (chalcogenide/opal) is then lifted-off and transferred onto the chalcogenide-glass disc at 225 °C, followed by removal of the template in hydrofluoric acid. The extra step introduced in this work (lift-off and transfer) allows a reproducible and large-area structure to be fabricated on a bulk chalcogenide glass. Complete infilling of the silica template is possible due to the nano-colloidal nature (particle size 2–8 nm) of the chalcogenide-glass solution and effective solvent release from the spin-coated chalcogenide film during post-annealing. The resulting chalcogenide-glass inverse-opal multilayer exhibits a Bragg peak at 670 nm with a reflectance 70%, while the inverse-opal monolayer shows anti-reflectance behaviour <2% in the near-infrared region (1215–1660 nm).