Rare-earth doped sol–gel derived oxyfluoride glass–ceramics: Structural and optical characterization

Glass–ceramics containing RE3+-doped BaF2 nanocrystals (RE = Eu, Sm, Dy, Ho and Pr) with the size below 10 nm size have been made by using the controlled crystallization at higher temperatures of the RE3+-doped SiO2–BaF2 xerogels. Photoluminescence measurements have indicated the incorporation of the RE3+ ions in both silica network and in the BaF2 nanocrystals. Thermoluminescence measurements have shown a peak whose position depends on the nature of RE3+-dopant as it follows: 140 °C (for Ho3+, Dy3+), 340 °C (for Sm3+) and 370 °C (for Eu3+); in Eu3+-doped SiO2 glass the TL peak is shifted to 383 °C. The peaks in glass–ceramics were assigned to the recombination of the electrons thermal released from the RE3+-electron traps located in both glass-matrix and BaF2 nanocrystals. Within the series the trivalent lanthanide ions act as increasingly deeper electron trapping centres.

Graphical abstractFigure optionsDownload full-size imageDownload high-quality image (172 K)Download as PowerPoint slideHighlights► Annealing of the rare-earth doped SiO2–BaF2 xerogel induces the crystallization of BaF2 nanocrystals. ► Rare-earth ions are embedded in the glass and in the BaF2 nanocrystals. ► Recombination of rare-earth related electron traps gives rise to thermoluminescence. ► Within the series the trivalent lanthanide ions act as increasingly deeper electron trapping centres.