1501902 | Scripta Materialia | 2007 | 4 Pages |
Abstract
The dissolution temperature of Nb(C, N) precipitates in a low-carbon microalloyed steel was quantitatively examined using electrical resistivity. The dissolution temperature of 0.02C–0.08Nb steel was about 1200 °C with isochronal annealing for 10 min and this was confirmed by transmission electron microscopic observation.
Related Topics
Physical Sciences and Engineering
Materials Science
Ceramics and Composites
Authors
J.S. Park, Y.K. Lee,