Electrical and structural properties of In-doped ZnO films deposited by RF superimposed DC magnetron sputtering system

Zinc-indium-oxide (ZIO) films were deposited on non-alkali glass substrates by RF superimposed DC magnetron sputtering with a ZIO (9.54 wt% In2O3 content) high-density, sintered target at room temperature. The electrical, structural and optical properties of the ZIO films deposited with different sputtering parameters were examined. The total power for RF superimposed DC magnetron sputtering was 80 W. The RF power ratio in the total sputtering power was changed from 0 to 100% in steps of 25%. The ZIO films deposited with a 100% RF discharge showed the lowest resistivity, 1.28×10−3 Ω cm, due to the higher carrier concentration. The ZIO film deposited at 50% RF power showed a relatively larger grain size and smaller FWHM. XPS suggested an increase in the level of In3+ substitution for Zn2+ in the ZnO lattice with increasing RF/(DC+RF) due to the low damage process. The average transmittance of all ZIO films in the visible light region was >80%. The increasing RF power portion of the total sputtering power led to a broadening of the optical band gap, which was attributed to the increase in carrier density according to Burstein–Moss shift theory.