Studies on structural and magnetic properties of Co-doped pyramidal ZnO nanorods synthesized by solution growth technique

Large-area arrays of highly oriented Co-doped ZnO nanorods with pyramidal hexagonal structure are grown on silica substrates by wet chemical decomposition of zinc–amino complex in an aqueous medium. In case of undoped ZnO with an equi-molar ratio of Zn2+/hexamethylenetetramine (HMT), highly crystalline nanorods were obtained, whereas for Co-doped ZnO, good quality nanorods were formed at a higher Zn2+/HMT molar ratio of 4:1. Scanning electron microscope (SEM) studies show the growth of hexagonal-shaped nanorods in a direction nearly perpendicular to the substrate surface with a tip size of ∼50 nm and aspect ratio around 10. The XRD studies show the formation of hexagonal phase pure ZnO with c-axis preferred orientation. The doping of Co ions in ZnO nanorods was confirmed by observation of absorption bands at 658, 617 and 566 nm in the UV–vis spectra of the samples. The optical studies also suggest Co ions to be present both in +2 and +3 oxidation states. From the photoluminescence studies, a defect-related emission is observed in an undoped sample of ZnO at 567 nm. This emission is significantly quenched in Co-doped ZnO samples. Further, the Co-doped nanorods have been found to show ferromagnetic behavior at room temperature from vibrating sample magnetometer (VSM) studies.