•UHMWPE/silane hybrids have been prepared and irradiated using gamma rays.•The structural analysis revealed the formation siloxane linkages in the hybrid.•The crystallinity, thermal stability and mechanical properties of hybrids were improved with irradiation.•The irradiated hybrids can be used in various high-strength applications.
This study has been carried to investigate the influence of gamma rays on the structural and physicochemical properties of UHMWPE/silane hybrid. UHMWPE was mixed with vinyltriethoxysilane (VTES) and compression molded sheets were irradiated at different doses of gamma rays. Fourier transform infrared spectroscopy indicated the formation of siloxane linkages in hybrids, which were found to be shifted towards lower wave number upon irradiation. The X-ray diffraction patterns showed significant increase in the percentage crystallinity of hybrid upon gamma irradiation, especially at 65 kGy absorbed dose. Scanning electron micrographs showed good consolidation and compaction with no surface defects. Moreover, the rough topography was changed to smooth ripple-like appearance upon γ-irradiation. Thermal analysis revealed that irradiated hybrids exhibited higher onset thermal degradation temperature, peak melting temperature, and crystalline lamellae thickness compared with the water treated hybrid. In addition, the tensile testing confirmed an increase of 41% and 133% in yield strength and Young's modulus in 100 kGy irradiated hybrid respectively than that of water treated hybrid. We hope that the irradiated UHMWPE/silane hybrids can be used in various high-strength applications such as total joint replacements, pickers for textile machinery, lining for coal chutes and dump trucks.
Graphical abstractFigure optionsDownload full-size imageDownload as PowerPoint slide