Polycrystalline ferrites with the general formula Ni0.95−xCdxCu0.05Fe2O4 in which x varies from 0.1 to 0.3 were synthesized by standard double sintering ceramic technique. The existence of single phase cubic spinel structure of ferrites was confirmed from XRD measurement. Surface morphology and compositional features were studied by SEM and EDX measurements. Absorption bands observed in FTIR spectra at 600 cm−1 (υ1) and 410 cm−1 (υ2) corresponds to vibrations of tetrahedral and octahedral complexes respectively. In the dc conductivity measurements the decrease of dc resistivity with increase of temperature indicates the semiconducting nature of ferrites. The dielectric measurement of the samples at room temperature studied in the frequency range 20 Hz to 1 MHz shows dispersion in the low frequency region and remains constant at high frequency region. However, the small polaron hoping type of conduction mechanism was inferred from the linear increase of ac conductivity. The magnetic properties of ferrites such as saturation magnetization, magnetic moment and Y–K angles was estimated as a function of cadmium content by VSM technique. The smaller value of Mr/Ms reveals the existence of multidomain (MD) particles in the ferrite samples.
Graphical abstractPolycrystalline ferrites with the general formula Ni0.95−xCdxCu0.05Fe2O4 in which x varies as 0.1, 0.2 and 0.3, were synthesized by standard double sintering ceramic technique. The existence of single phase cubic spinel structure of ferrites was confirmed from XRD measurement. Surface morphology and compositional features were studied by SEM and EDAX measurements. FTIR spectrum of spinel ferrites corresponds to vibrations of tetrahedral and octahedral complexes respectively. In the dc conductivity measurements the decrease of dc resistivity with increase of temperature indicates the semiconducting nature of ferrites. The dielectric measurement of the samples at room temperature was studied in the frequency range 20 Hz to 1 MHz. The dielectric constant shows dispersion in the low frequency region and remains constant at high frequency region. However, the small polaron hoping type of conduction mechanism was inferred from the linear increase of ac conductivity. The magnetic properties of ferrites such as saturation magnetization, magnetic moment and Y–K angles was estimated as a function of cadmium content by VSM technique. The smaller value of Mr/Ms reveals the existence of multidomain (MD) particles in the ferrite samples.Figure optionsDownload full-size imageDownload as PowerPoint slideHighlights► Polycrystalline ferrites with composition Ni0.95−xCdxCu0.05Fe2O4 have been successfully synthesized by ceramic method. ► The presence of Ni, Cd, Cu, Fe and O elements in the ferrite samples were confirmed from EDX measurements. ► Saturation magnetization, magnetic moment and Y–K angles are found to increase with cadmium content. ► The small values of Mr/Ms suggest the existence of MD particles in all the samples. ► These ferrites show good response in electric and magnetic properties.