The effect of Ti serving as an activator in a eutectic Ag–Cu alloy filler metal in dissimilar laser-brazed joints of isotropic graphite and a WC–Co alloy on the joint strength and the interface structure of the joint is investigated in this study. To evaluate the joint characteristics, the Ti content in the filler metal was increased from 0 to 2.8 mass%. The laser brazing was carried out by irradiating a laser beam selectively on the WC–Co alloy plate in Ar atmosphere. The threshold content of Ti required to join isotropic graphite to WC–Co alloy was 0.4 mass%. The shear strength at the brazed joint increased rapidly with increasing Ti content up to 1.7 mass%, and a higher Ti content was found to be likely to saturate the shear strength to a constant value of about 14 MPa. The isotropic graphite blocks also fractured at this content. The concentration of Ti observed at the interface between isotropic graphite and the filler metal indicates the formation of an intermetallic layer of TiC.
► Ti was required in the filler metal for brazing graphite to WC–Co alloy. ► The shear strength of the joint increased with Ti content up to 1.7 mass%. ► Ti concentrated at the interface of graphite/filler metal. ► TiC was formed at the interface of graphite/filler metal.