PbS micro- and nanoparticles were synthesized by a simple precipitation reaction of lead nitrate with thioacetamide in hydrosoluble polymer water solutions. The effects of four water soluble polymers: polyacrylamide (PAM), polyvinyl alcohol (PVA), polyethylene glycol (PEG) and poly-N-vinyl pyrrolidone (PVP) on the PbS crystallites morphology and structural properties were investigated by scanning electron microscopy (SEM) and X-ray diffraction (XRD). It was found that for the PbS particles obtained in the PVA, PEG and PVP, the (2 0 0) diffraction peak of the nanocrystals becomes dominant. The highest texture in the [2 0 0] direction was observed for the crystallites obtained in the presence of PVP. Polydisperse PbS particles with cubic morphology and size ranging from 100 nm to several microns are obtained in the case of PAM and PEG. Monodisperse cubic PbS crystallites with an average size of 200 nm are formed in the presence of PVA and PVP.
► PbS crystallites were synthesized in hydrosoluble polymers (PAM, PEG, PVA, PVP). ► Polymer type plays an important role in the morphology and structural properties of the PbS crystallites. ► Polydisperse PbS particles of size from 100 nm to several microns (PAM and PEG). ► Monodisperse PbS crystallites of about 200 nm size (PVA and PVP). ► PbS nanoparticles are highly textured in the [2 0 0] direction.