Modelling mixed-mode fracture in poly(methylmethacrylate) using peridynamics

In this work the predictive abilities of peridynamics were checked against experimental results in the case of mixed-mode failure of brittle polymers. Pre-cracked poly(methylmethacrylate) (PMMA) samples were tested using different specimens, in order to obtain Mode I, Mixed-Mode and Mode II loading conditions. The material was assumed to behave according to a peridynamics brittle elastic material model; the parameters needed to calibrate the elastic behavior were determined from Mode I tests, as was the critical stretch.The peridynamics simulations of mixed-mode tests were able to catch the correct fracture initiation load and to provide a fair description of the crack path under different conditions. The peridynamics model was also able to qualitatively capture the typical “nail” shape assumed by the crack front during propagation.