The high temperature behavior of SrSO4, SrCO3 and Al2O3 mixtures was studied. A mixture of 1:1 mole of SrSO4 and mechanically activated SrCO3 was mixed and characterized using thermal gravimetric analysis. Some samples were uniaxially pressed and sintered at 1100, 1200 and 1300 °C for 8 h and then analyzed using X-ray diffraction and scanning electron microscopy. Additionally, a mixture of SrSO4:SrCO3:Al2O3 was uniaxially pressed and sintered at 1500 °C. The decomposition temperature of SrCO3 was decreased 18° by milling for 180 min. Samples sintered at 1300 °C showed a microstructure free of porosity. X-ray diffraction analysis showed the presence of SrO and SrSO4 after sintering at 1100, 1200 and 1300 °C. The mixture containing alumina showed the formation of a strontium aluminum oxide sulfate compound in addition to strontium aluminate.