Effect of Ti/Sc atom ratio on heterogeneous nuclei, microstructure and mechanical properties of A357-0.033Sr alloys

A systematic study on heterogeneous nucleation, microstructure and mechanical properties of A357-0.033Sr alloys with different Ti/Sc atom ratio was carried out. According to the obtained results, a Ti/Sc atom ratio up to 1:1 did not show much change in the heterogeneous nuclei but at a higher atom ratio level, heterogeneous nuclei have a great change in chemical composition and morphology (from strip Ti-rich phase to the particle-like Ti-rich phase). In addition, compared to the other four alloys studied, the A357-0.033Sr-0.30Sc-0.35Ti alloy with 1:1 atom ratio has the smallest grain size (88 µm), optimum microstructure (morphology, size and distribution of eutectic Si), densest core-shell Al3(Sc, Ti), all of which result in the best mechanical properties. Its tensile strength and elongation reach 287 MPa and 3.62% respectively, showing about 11% and 84% increases compared with A357-0.033Sr alloy.