Cross accumulative roll bonding-A novel mechanical technique for significant improvement of stir-cast Al/Al2O3 nanocomposite properties

Lightweight metal-matrix nanocomposites (MMNCs-metal matrix with nanosized ceramic particles) can be of significance for automobile, aerospace, and numerous other applications. There are some problems in obtaining suitable mechanical properties of MMNCs, including weak bonding between reinforcement and matrix, non-uniformity of reinforcement nanoparticles and high porosity content. In this study, aluminum/alumina nanocomposite was fabricated by stircasting method. Subsequently, cross accumulative roll bonding (CARB) process was used as an effective method for refinement of microstructure and improvement of mechanical properties. The microstructural evolution and the mechanical properties of the nanocomposites during various CARB cycles were examined by the Archimedes method, X-ray defractometer, scanning electron microscopy and tensile testing. The results showed that the microstructure of the nanocomposite after eight cycles of CARB had an excellent distribution of alumina nanoparticles in aluminum matrix without any remarkable porosity. The X-ray diffraction results showed that the crystallite size of the nanocomposite was 71 nm by employing eight cycles of CARB technique. Mechanical experiment also indicated that the ultimate tensile strength and the elongation of the nanocomposite increased as the number of CARB cycles increased. After eight CARB cycles, ultimate tensile strength and the elongation values reached 344 MPa and 6.4%, which were 3.13 and 3.05 times greater than those of as-cast nanocomposites, respectively.