Article ID | Journal | Published Year | Pages | File Type |
---|---|---|---|---|
1576091 | Materials Science and Engineering: A | 2013 | 7 Pages |
Abstract
The effects of tempering on surface topography and dislocation configuration of 6061-T651 aluminum alloy by laser shock processing (LSP) were investigated at the elevated temperatures. Surface topography and surface roughness were tested by a Surfcom 130A-Monochrome surface rough-meter. Morphologies of precipitated phases were monitored by scanning electron microscopy (SEM), and the dislocation configurations of samples after LSP were characterized by transmission electron microscope (TEM). The results showed that LSP had a beneficial effect on micro-hardness at elevated temperature. There was a little change of the surface roughness as subjected to LSP. The main strengthening mechanism of micro-hardness was dislocation strengthening and fine grain strengthening, and precipitated phase strengthening was the main strengthening mechanism at elevated temperature. “Dislocation polymorphism transformation” (DPT) effect was affirmed at elevated temperature, and the elevated temperature was principal element for inducing the DPT effect of 6061-T651 aluminum alloy by LSP.
Related Topics
Physical Sciences and Engineering
Materials Science
Materials Science (General)
Authors
X.D. Ren, L. Ruan, S.Q. Yuan, N.F. Ren, L.M. Zheng, Q.B. Zhan, J.Z. Zhou, H.M. Yang, Y. Wang, F.Z. Dai,