The trapping of hydrogen by VC precipitates and structural defects in high strength Fe–Mn–C steel was studied by small angle neutron scattering. No interaction between H and V in solid solution has been detected but a significant interaction between H and structural defects introduced by plastic deformation has been measured. This last effect was reversible upon outgassing of the H. Moreover a significant interaction between H and VC precipitates has been measured; 5 ppm wt. of H could be trapped in the precipitates. This is consistent with the homogeneous trapping of H within the precipitates rather than at the precipitate/matrix interface.
► SANS was used to study the interaction between H and a Fe–Mn–C steel containing V. ► No interaction between H and V in solid solution has been detected. ► A reversible interaction between H and structural defects has been measured. ► 5 ppm wt. of H can be trapped in the VC nanoprecipitates.