Aromatic-aliphatic polyamide/montmorillonite clay nanocomposite materials: Synthesis, nanostructure and properties

New type of aromatic-aliphatic polyamide/montmorillonite nanocomposites were produced using solution intercalation technique in dimethylacetamide. The modification of clay was carried out with ammonium salt of long chain alkyl amine. The nanocomposites were probed for organoclay dispersion, mechanical, thermal and water absorption measurements. Formation of delaminated and intercalated nanostructures was confirmed by X-ray diffraction and TEM studies. Improvement in tensile strength and modulus was observed for nanocomposites with optimum organoclay content (8-wt.%). Thermogravimetric analysis indicated an increase in thermal stability of nanocomposites as compared to pristine polyamide. Differential scanning calorimetric results revealed increase in glass transition temperatures (Tg) with augmenting organoclay in the nanocomposites. Water uptake of the nanocomposites reduced than the neat polyamide rendering decreased permeability.