| Article ID | Journal | Published Year | Pages | File Type |
|---|---|---|---|---|
| 1580829 | Materials Science and Engineering: A | 2010 | 5 Pages |
Abstract
The effects of casting temperature on microstructure and mechanical properties of as-cast 3 mm-diameter Zr64.9Al7.9Ni10.7Cu16.5 and Zr47Cu37.5Ag7.5Al8 alloys were investigated. It was found that crystalline phases were precipitated in amorphous matrix as casting temperature increased. The compressive strength and Hv of as-cast Zr64.9Al7.9Ni10.7Cu16.5 and Zr47Cu37.5Ag7.5Al8 alloys increased slightly when casting temperature increased. However, ultrahigh casting temperature resulted in formation of hard crystalline phase in metallic glass matrix, which caused increase of hardness and density, but decrease of compressive strength.
Related Topics
Physical Sciences and Engineering
Materials Science
Materials Science (General)
Authors
J. Mao, H.F. Zhang, H.M. Fu, A.M. Wang, H. Li, Z.Q. Hu,